Low and moderate dose gamma-irradiation and annealing impact on electronic and electrical properties of AlGaN/GaN high electron mobility transistors

To understand the effects of Co-60 gamma-irradiation, systematic studies were carried out on n-channel AlGaN/GaN high electron mobility transistors. Electrical testing, combined with electron beam-induced current measurements, was able to provide critical information on defects induced in the material as a result of gamma-irradiation. It was shown that at low gamma-irradiation doses, the minority carrier diffusion length in AlGaN/GaN exhibits an increase up to approximate to 300Gy. The observed effect is due to longer minority carrier (hole) life time in the material's valence band as a result of an internal electron irradiation by Compton electrons. However, for larger doses of gamma irradiation (above 400Gy), deteriorations in transport properties and device characteristics were observed. This is consistent with the higher density of deep traps in the material's forbidden gap induced by a larger dose of gamma-irradiation. Moderate annealing of device structures at 200 degrees C for 25min resulted in partial recovery of transport properties and device performance.