Pulsed Laser Deposition of Ba x Sr 1−x TiO 3 Films on MgO, LaAlO 3 and SrTiO 3 for Tunable Microwave Applications

Single phase BaxSr 1−x TiO 3 (BST) films (∼0.5-7 μm thick) have been deposited onto single crystal substrates (MgO, LaAlO 3 , SrTiO 3 ) by pulsed laser deposition. Silver interdigitated electrodes were deposited on top of the ferroelectric film. The room temperature capacitance and dielectric Q (1/tanδ) of the film have been measured as a function of electric field (≤80 kV/cm) at 1 - 20 GHz. The dielectric properties of the film are observed to strongly depend on substrate type and post-deposition processing. After annealing (≤1000° C), it was observed that the dielectric constant and % tuning decreased and the dielectric Q increased for films deposited onto MgO, and the opposite effect was observed for films deposited onto LaA1O 3 . Presumably, this change in dielectric properties is due to the changes in film stress. Very thin (∼50 Å) amorphous BST films were successfully used as a stress-relief layer for the subsequently deposited crystalline BST (∼5000 Å) films to maximize % tuning and dielectric Q. Films have been deposited from stoichiometric targets and targets that have excess Ba and Sr. The additional Ba and Sr has been added to the target to compensate for deficiencies in Ba and Sr observed in the deposited BST (x=0.5) films. Films deposited from compensated targets have higher dielectric constants than films deposited from stoichiometric targets. Donor/acceptor dopants have also been added to the BST target (Mn, W, Fe ≤4 mol.%) to further improve the dielectric properties. The relationship between the dielectric constant, the dielectric Q, the change in dielectric constant with electric field is discussed.