Effect of Oxygen Exposure and Deposition Environment on Thermal Stability of Ta Barriers To Cu Penetration.
ELECTRONIC PACKAGING MATERIALS SCIENCE V(1990)
摘要
The effect of deposition pressure and controlled oxygen dosing on the diffusion barrier performance of thin film Ta to Cu penetration was investigated. In-situ resistivity, Auger compositional profiling, scanning electron microscopy and cross-sectional transmission electron microscopy were used to determine the electrical, chemical and structural changes that occur in Cu/Ta bilayers on Si upon heating. A 20 nm Ta barrier allowed the penetration of Cu at temperatures ranging from 320 to 630°C depending on processing conditions. Barrier failure temperature is dependent upon the deposition pressure and oxygen contamination at the Ta/Cu interface. This indicates the importance of understanding how deposition conditions affect diffusion barrier performance.
更多查看译文
关键词
cu penetration,stability barriers,deposition environment,thermal stability
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要