Calcination Influence on the Structure and Morphology of Zirconia Synthesized by Combustion Reaction

This research aims to synthesize ZrO2 by combustion reaction in batches of 15 g of the product and to evaluate the calcination influence on the structural and morphological characteristic about synthesized sample. For the synthesis of ZrO2, the stoichiometry of phase was established in accordance with the propellants and explosives chemical concept, whereas the stoichiometric coefficient phi =1. After the synthesis, the sample as synthesized was calcined at 600 and 700 degrees C and subsequently characterized by XRD, SEM, textural analysis (BET) and FTIR. The results have shown to the sample as synthesized and then calcined at 600 degrees C the majority phase formation of orthorhombic zirconia with monoclinic phase dashes. The temperature increase to 700 degrees C, has been transformed a part of the orthorhombic ZrO2 to a monoclinic phase, contributing to a surface area reduction of the samples, showing irregular agglomerates in morphology, with adsorption/desorption isotherms type IV and mesoporosity characteristic.