Influence of Selenium Evaporation Temperature on the Structure of Cu2znsnse4 Thin Film Deposited by A Co-Evaporation Process
Journal of Semiconductors/Journal of semiconductors(2015)
摘要
Cu2ZnSnSe4 (CZTSe) thin film solar cells have been fabricated using a one-step co-evaporation technique. The structural properties of polycrystalline CZTSe films deposited at different selenium evaporation temperatures (T-Se) have been investigated using X-ray diffraction spectra, scanning electron microscopy, and atomic force microscopy. A relationship between T-Se and the secondary phases deposited in the initial stage is established to explain the experimental observations. The Se flux is not necessarily increased too much to reduce Sn loss and the consumption of Se during fabrication could also be reduced. The best solar cell, with an efficiency of 2.32%, was obtained at a medium T-Se of 230 degrees C (active area 0.34 cm(2)).
更多查看译文
关键词
Cu2ZnSnSe4,one-step co-evaporation,selenium flux,thin film solar cells,Sn loss
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要