Emission Wavelength Dependence of Internal Quantum Efficiency in InGaN Nanowires

The internal quantum efficiency (IQE) of InGaN nanowires with different emission wavelength of 485, 515, 555, and 580 nm has been studied by means of photoluminescence (PL) spectroscopy. It was found from the analysis of IQE as a function of excitation power density that the IQE was unchanged at about 100% under weak excitation conditions at low temperature. This indicated that the effects of nonradiative recombination processes were negligibly small at low temperature. Moreover, the IQE increased from 5 to 12% with increasing emission wavelength from 485 to 580 nm. Since the clear correlation between the IQE and the PL blue shift due to band filling effects of localized states was observed, the increase in the IQE reflected the increase in the effect of exciton localization with increasing indium composition. (C) 2013 The Japan Society of Applied Physics