Residual Stress Measurements Via Neutron Diffraction of Additive Manufactured Stainless Steel 17-4 PH
Data in brief(2017)
摘要
Neutron diffraction was employed to measure internal residual stresses at various locations along stainless steel (SS) 17-4 PH specimens additively manufactured via laser-powder bed fusion (L-PBF). Of these specimens, two were rods (diameter=8mm, length=80mm) built vertically upward and one a parallelepiped (8×80×9mm3) built with its longest edge parallel to ground. One rod and the parallelepiped were left in their as-built condition, while the other rod was heat treated. Data presented provide insight into the microstructural characteristics of typical L-PBF SS 17-4 PH specimens and their dependence on build orientation and post-processing procedures such as heat treatment. Data have been deposited in the Data in Brief Dataverse repository (doi:10.7910/DVN/T41S3V).
更多查看译文
关键词
Additive manufacturing,Selective Laser Melting (SLM),Powder bed fusion,Residual stress,Heat treatment, microstructure
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要