Microstructure, Phase Occurrence, and Corrosion Behavior of As-Solidified and As-Annealed Al-Pd Alloys

In the present work, we studied the microstructure, phase constitution, and corrosion performance of Al 88 Pd 12 , Al 77 Pd 23 , Al 72 Pd 28 , and Al 67 Pd 33 alloys (metal concentrations are given in at.%). The alloys were prepared by repeated arc melting of Al and Pd granules in argon atmosphere. The as-solidified samples were further annealed at 700 °C for 500 h. The microstructure and phase constitution of the as-solidified and as-annealed alloys were studied by scanning electron microscopy, energy-dispersive x-ray spectroscopy, and x-ray diffraction. The alloys were found to consist of (Al), ε n (~ Al 3 Pd), and δ (Al 3 Pd 2 ) in various fractions. The corrosion testing of the alloys was performed in aqueous NaCl (0.6 M) using a standard 3-electrode cell monitored by potentiostat. The corrosion current densities and corrosion potentials were determined by Tafel extrapolation. The corrosion potentials of the alloys were found between − 763 and − 841 mV versus Ag/AgCl. An active alloy dissolution has been observed, and it has been found that (Al) was excavated, whereas Al in ε n was de-alloyed. The effects of bulk chemical composition, phase occurrence and microstructure on the corrosion behavior are evaluated. The local nobilities of ε n and δ are discussed. Finally, the conclusions about the alloy’s corrosion resistance in saline solutions are provided.