Insight Into Understanding Dielectric Behavior Of A Zn-Mof Using Variable-Temperature Crystal Structures, Electrical Conductance, And Solid-State C-13 Nmr Spectra

A Zn-based metal-organic framework (MOF)/porous coordination polymer (PCP), (EMIM)[Zn(SIP)] (1) (SIP3 = 5-sulfoisophthalate, EMIM+ = 1-ethyl-3-methylimidazolium), was synthesized using the ionothermal reaction. The Zn2+ ion adopts distorted square pyramid coordination geometry with five oxygen atoms from three carboxylates and one sulfo group. One of two carboxylates in SIP3 serves as a mu(2)-bridge ligand to link two Zn2+ ions and form the dinuclear SBU, and such SBUs are connected by SIP3 ligands to build the three-dimensional framework with rutile (rtl) topology. The cations from the ion-liquid fill the channels. This MOF/PCP shows two-step dielectric anomalies together with two-step dielectric relaxations; the variable-temperature single-crystal structure analyses disclosed the dielectric anomaly occurring at ca. 280 K is caused by an isostructural phase transition. Another dielectric anomaly is related to the dynamic disorder of the cations in the channels. Electric modulus, conductance, and variable-temperature solid-state C-13 CP/MAS NMR spectra analyses revealed that two-step dielectric relaxations result from the dynamic motion of the cations as well as the direct-current conduction and electrode effect, respectively.