The synthesis and characterization of 1 1 1 1 type diluted ferromagnetic semiconductor (La(1-x)Ca(x))(Zn(1-x) Mn(x))AsO.

We report the synthesis and characterization of a bulk form diluted magnetic semiconductor, (La(1-x)Ca(x))(Zn(1-y) Mn(y))AsO, with a layered crystal structure isostructural to that of the 1 1 1 1 type Fe-based high-temperature superconductor LaFeAsO and the antiferromagnetic LaMnAsO. With Ca and Mn codoping into LaZnAsO, the ferromagnetic ordering occurs below the Curie temperature T(c) ∼30 K. Taking advantage of the decoupled charge and spin doping, we investigate the influence of carrier concentration on the ferromagnetic ordering state. For a fixed Mn concentration of 10%, T(c) increases from 24 K to 30 K when the Ca concentration increases from 5% to 10%. Further increase of Ca concentration reduces both the coercive field and saturation moment. Muon spin relaxation measurements confirm the ferromagnetically ordered state, and clearly demonstrate that La(1-x)Ca(x))(Zn(1-y) Mn(y))AsO shares a common mechanism for the ferromagnetic exchange interaction with (Ga,Mn)As. Neutron scattering measurements show no structural transition in (La(0.90)Ca(0.10))(Zn(0.90)Mn(0.10)) AsO below 300 K.