Fabrication of Fe2O3/TiO2 oxygen carriers for chemical looping combustion and hydrogen generation

The characteristics and application of TiO2-supported Fe2O3 oxygen carriers were investigated for chemical looping combustion (CLC) and hydrogen generation (CLHG) in this study. Prepared Fe2O3/TiO2 oxygen carriers with 20-30 wt% of TiO2 were demonstrated to achieve satisfactory results even after 30-cycle operation by thermogravimetric analyzer (TGA). Oxygen carriers contain more than 33 wt% TiO2 were observed to be more porous and fragile after continuous high-temperature operation. Conversely, the reactivity of oxygen carriers contain less 10 wt% TiO2 was rapidly decayed after operated for merely 3 redox cycles because of their dense structure. The CO2 and H-2 conversions through syngas combustion and steam oxidation, respectively, for experiments were demonstrated to be feasible using sieved oxygen carriers at higher operation temperatures from 400 to 1000 degrees C in fixed bed reactor (FBR) system.