Enhanced Piezoelectric Properties and Temperature-Insensitive Strain Behavior of < 001 > -Textured Knn-Based Ceramics

In this study, <001>-textured 0.99(K0.5Na0.5)0.95Li0.05Nb0.93Sb0.07O3−0.01CaZrO3 [abbreviated as 0.99KNLNS-0.01CZ] lead-free ceramics were prepared by templated grain growth (TGG) using plate-like NaNbO3 templates and sintered by a two-step sintering process with different soaking time. All textured samples with high Lotgering factor (f >85%) presented orthorhombic and tetragonal coexisting phase, and the proportion of orthorhombic phase was varied with prolonged soaking time. A large piezoelectric constant d33 (~ 310 pC/N) was obtained in the textured samples with a 12h soaking time, which was almost twice larger compared to the randomly oriented one. Furthermore, the field-induced piezoelectric strain coefficient d33*(~ 440pm/V) of the textured ceramics with 6h soaking time was larger than the value of randomly oriented one (~ 298pm/V) at room-temperature. Enhanced piezoelectric response and good temperature stability prove that <001>-textured 0.99KNLNS-0.01CZ ceramics are promising candidates in the field of lead-free piezoelectric materials.