Preparation, Foaming and Characterization of Poly(l-lactic acid))/Poly(d-lactic acid)-Grafted Graphite Oxide Blends

Commercial poly(l-lactic acid) (PLLA) was blended with different contents of graphene oxide-graft-poly(d-lactic acid) (GO-g-PDLA), which was synthesized via ring-opening polymerization using modified GO as initiator. PLLA and PLLA/GO-g-PDLA blend foams were prepared in a batch process via varying-temperature mode using supercritical carbon dioxide as physical foaming agent. The results showed that the addition of GO-g-PDLA in PLLA leads to the formation of stereocomplex (sc)-crystallites. Increase in the GO-g-PDLA content enhances the IR absorption, diffraction peak and melting peak corresponding to the sc-crystallites. The addition of GO-g-PDLA to PLLA leads to the decrease of the cell diameter, increase of the cell density and to a little change in expansion ratio, which is attributed to the fact that the enhancement of PLLA crystallization restricts cell growth and GO-g-PDLA acts as nucleation point.