Connecting 1D and 2D Confined Polymer Dynamics to Its Bulk Behavior Via Density Scaling

Under confinement, the properties of polymers can be much different from the bulk. Because of the potential applications in technology and hope to reveal fundamental problems related to the glass-transition, it is important to realize whether the nanoscale and macroscopic behavior of polymer glass-formers are related to each other in any simple way. In this work, we have addressed this issue by studying the segmental dynamics of poly(4-chlorostyrene) (P4ClS) in the bulk and upon geometrical confinement at the nanoscale level, in either one- (thin films on Al substrate) or two- (within alumina nanopores) dimensions. The results demonstrate that the segmental relaxation time, irrespective of the confinement size or its dimensionality, can be scaled onto a single curve when plotted versus ργ/T with the same single scaling exponent, γ = 3.1, obtained via measurements at high pressures in bulk. The implication is that the macro- and nanoscale confined polymer dynamics are intrinsically connected and governed by the same underlying rules.