Fe3O4 nanoparticles as the saturable absorber for a mode-locked fiber laser at 1558 nm

We demonstrated a mode-locked erbium doped fiber laser (EDFL) operating at 1558 nm by exploiting ferroferric-oxide nanoparticles (FONPs) as the saturable absorber (SA) material. FONPs, with an average diameter of similar to 20nm, were prepared by a thermal decomposition method, then mixed with sodium carboxymethylcelluose to form an FONP film. The FONP SA was fabricated through a sandwiched FONP film between two fiber connectors. By inserting the FONPs SA into an EDFL cavity pumped by a 980nm laser diode, stable passive mode-locking was achieved with a threshold pump power of similar to 120 mW. The obtained mode- locked laser had a central wavelength of similar to 1558 nm, a spectral bandwidth of similar to 0.8 nm, a pulse width of similar to 4.35 ns, and a repetition rate of similar to 37.32 MHz. Furthermore, a maximum average power of similar to 17 mW was obtained for a pump power of 340 mW. To the best of our knowledge, this is the first time that it has been demonstrated that FONPs can be used for constructing mode-locked fiber lasers.