Optimization of Transistor Characteristics and Charge Transport in Solution Processed ZnO Thin Films Grown from Zinc Neodecanoate

Solution processing of metal oxide-based semiconductors is an attractive route for low-cost fabrication of thin films devices. ZnO thin films were synthesized from one-step spin coating-pyrolysis technique using zinc neodecanoate precursor. X-ray diffraction (XRD), UV–visible optical transmission spectrometry and photoluminescence spectroscopy suggested conversion to polycrystalline ZnO phase for decomposition temperatures higher than 400 °C. A 15 % precursor concentration was found to produce optimal TFT performance on annealing at 500 °C, due to generation of sufficient charge percolation pathways. The device performance was found to improve upon increasing the annealing temperature and the optimal saturation mobility of 0.1 cm 2 V −1 s −1 with I ON /I OFF ratio ~ 10 7 was achieved at 700 °C annealing temperature. The analysis of experimental results based on theoretical models to understand charge transport envisaged that the grain boundary depletion region is major source of deep level traps and their effective removal at increased annealing temperature leads to evolution of transistor performance. Graphic Abstract Single-step spin coating-pyrolysis synthesis of ZnO thin films from non-aqueous precursor zinc neodecanoate has been investigated for transistor applications.