Controlling the Facet of ZnO during Wet Chemical Etching Its (0001 over bar ) O-Terminated Surface

Special surface plays a crucial role in nature as well as in industry. Here, the surface morphology evolution of ZnO during wet etching is studied by in situ liquid cell transmission electron microscopy and ex situ wet chemical etching. Many hillocks are observed on the (0001 over bar ) O-terminated surface of ZnO nano/micro belts during in situ etching. Nanoparticles on the apex of the hillocks are observed to be essential for the formation of the hillocks, providing direct experimental evidence of the micromasking mechanism. The surfaces of the hillocks are identified to be {011 over bar 3 over bar } crystal facets, which is different from the known fact that {011 over bar 1 over bar } crystal facets appear on the (0001 over bar ) O-terminated surface of ZnO after wet chemical etching. O-2 plasma treatment is found to be the key factor for the appearance of {011 over bar 3 over bar } instead of {011 over bar 1 over bar } crystal facets after etching for both ZnO nano/micro belts and bulk materials. The synergistic effect of acidic etching and O-rich surface caused by O-2 plasma treatment is proposed to be the cause of the appearance of {011 over bar 3 over bar } crystal facets. This method can be extended to control the surface morphology of other materials during wet chemical etching.