Conductivity enhancement of carbon aerogel by modified gelation using self additive

Carbon aerogels having high surface area and open pore structure are being studied for many electrochemical applications such as fuel cells and super capacitors. Moderate electrical conductivity of resorcinol - formaldehyde (R-F) derived carbon aerogel limits its utility in these applications. The current manuscript briefs about the synthesis of composite carbon aerogel using carbon aerogel itself as additive during gelation of water based carbon aerogel and study the effect on its conductivity and surface properties. The additive carbon aerogel was synthesized and pre-treated at higher temperature to achieve enhancement in conductivity. The composite carbon aerogel (CCA) samples were characterized for surface area properties, morphology, electrical conductivity and specific capacitance. The surface area properties of CCA showed improvement and specific surface area of similar to 1798 m(2)/g with total pore volume of 1.7 cm(3)/g. was obtained. The electrical conductivity of the composite carbon aerogel with 5 wt % additive showed improvement over the plain carbon aerogel with respective values of 144 S/m and 128 S/m. The specific capacitance evaluated for CA and CCA are 102 and 118 F/g at scan rate of 10mV/s with improvement of similar to 16%.