Effect Of Scanning Speed On Microstructure And Properties Of 30cr3ni2 Alloy Steel Prepared By Direct Laser Deposition
AOPC 2019: ADVANCED LASER MATERIALS AND LASER TECHNOLOGY(2019)
摘要
The 30Cr3Ni2 alloy steel samples were prepared by direct laser deposition (DLD) technology with different scanning speeds. The microstructure and mechanical properties of the samples were studied by metallographic microscope, scanning electron microscopy, energy dispersive spectroscopy, microhardness tester and electronic universal material tester. The results show that when the laser power was 2500W and the scanning speed was 10mm/s, the fabricated sample mainly consisted of granular bainite(GB) with (Fe,Cr)(7)C-3 carbide. The average hardness value was 341HV, the tensile strength was 875Mpa, the yield strength was 867Mpa, and the elongation was 3.9%. This study provides the basis for the further development of alloy steel produced by DLD.
更多查看译文
关键词
direct laser deposition,30Cr3Ni2 alloy steel,scanning speed,microstructure and properties,bainite,carbide
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要