Nanoscale Mg-B via Surfactant Ball Milling of MgB2: Morphology, Composition, and Improved Hydrogen Storage Properties
JOURNAL OF PHYSICAL CHEMISTRY C(2020)
摘要
Metal borides have attracted the attention of researchers due to their useful physical properties and unique ability to form high hydrogen-capacity metal borohydrides. We demonstrate improved hydrogen storage properties of a nanoscale Mg-B material made by surfactant ball milling MgB2 in a mixture of heptane, oleic acid, and oleylamine. Transmission electron microscopy data show that Mg-B nanoplatelets are produced with sizes ranging from 5 to 50 nm, which agglomerate upon ethanol washing to produce an agglomerated nanoscale Mg-B material of micron-sized particles with some surfactant still remaining. X-ray diffraction measurements reveal a two-component material where 32% of the solid is a strained crystalline solid maintaining the hexagonal structure with the remainder being amorphous. Fourier transform infrared shows that the oleate binds in a "bridge-bonding" fashion preferentially to magnesium rather than boron, which is confirmed by density functional theory calculations. The Mg-B nanoscale material is deficient in boron relative to bulk MgB2 with a Mg-B ratio of similar to 1:0.75. The nanoscale MgB0.75 material has a disrupted B-B ring network as indicated by X-ray absorption measurements. Hydrogenation experiments at 700 bar and 280 degrees C show that it partially hydrogenates at temperatures 100 degrees C below the threshold for bulk MgB2 hydrogenation. In addition, upon heating to 200 degrees C, the H-H bond-breaking ability increases similar to 10-fold according to hydrogen-deuterium exchange experiments due to desorption of oleate at the surface. This behavior would make the nanoscale Mg-B material useful as an additive where rapid H-H bond breaking is needed.
更多查看译文
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要