Improving Properties of Poly(vinylidene fluoride) by Adding Expanded Graphite without Surface Modification via Water-Assisted Mixing Extrusion

Expanded graphite (EG) is introduced into poly(vinylidene fluoride) (PVDF) by melt mixing extrusion with water injection. The results demonstrate that the unfunctionalized EG in composite prepared with water injection exbibits better dispersion than that in the one prepared without water injection due to the promoting role of water during extrusion. Thus, the PVDF/EG composite with loading of 4 wt% prepared by water-assisted mixing extrusion (WAME) exhibits electrical conductivity of about three orders of magnitude higher than the neat PVDF and one order of magnitude higher than the one prepared without water injection. Comparing to the neat PVDF, the thermal conductivity of the composites prepared with and without water injection is increased by 101.5% and 75.0%, respectively. The introduced EG leads to increased Young's modulus and tensile strength especially for the composite prepared by WAME. The present work indicates that WAME can promote the dispersion of EG in PVDF matrix without any extra functionalization.