Reduction and Nitridation of Iron/Vanadium Oxides by Ammonia Gas: Mechanism and Preparation of FeV45N Alloy

The steel micro-alloyed with ferrovanadium nitride has extremely superior properties that make it widely utilized in structural components, construction and aircraft. The conventional methods for synthesizing ferrovanadium nitride include nitridation of pure ferrovanadium alloy or carbothermal nitridation of metallic oxides, using nitrogen or ammonia gas as nitrogen sources. In this study, ferrovanadium nitride (FeV45N) was prepared by direct reduction and nitridation of the corresponding metal oxides with ammonia as the reductant and nitrogen source. This method avoids the introduction of other impurity elements, except the negligible trace elements accompanied with the raw materials. The thermodynamics of the reduction and nitridation process were initially analyzed. During the subsequent ammonia reduction process, the FeV45N powders were successfully obtained at 1273 K for 6 h. The obtained powders were pressed into cylindrical briquettes by hot pressing (HP) at 1473 K for 1 h in vacuum. In the investigation, the X-ray diffraction and morphological analysis of the products was also carried out, and the reaction mechanisms were discussed in detail. The nitrogen content of the final product can reach 11.85 wt. %, and the residual oxygen content can be reduced to 0.25 wt. %. By sintering, the density of the alloy can reach 5.92 g/cm3.