Morphologies, interfacial interaction and mechanical performance of super-tough nanostructured PK/PA6 blends

Nanostructured polyketone (PK)/polyamide 6 (PA6) blends can be readily prepared via melt blending technologies and exhibit ultra-high toughness when PA6 is present as the nanoscale phase domains. When PA6 content is 30 vol%, the impact strength of the blends increases from 21.4 kJ/m(2) of pure PK to 103.2 kJ/m(2). The impact strength of the PK/PA6 blends with a 5:5 composition ratio reaches as high as 113 kJ/m(2). The strong intermolecular force between PK and PA6 molecular chains enables the PA6 nanophase to cavitate to dissipate a significant amount of impact energy and effectively prevents the crack propagation or even terminates the cracks. The fracture mechanism of the PK/PA6 blends was further examined by the essential work of fracture method which proves that PK/PA6 blends show improved ability to prevent crack propagation. This work may deepen the understanding of polymer blend systems with strong hydrogen bonding interaction.