Pet/Cloisite (R) 15a Composite Fibers - Studies On The Structure And The Flame Inhibition Mechanism

The improvement of poly(ethylene terephthalate) (PET) fibers flame retardancy is usually achieved by using antipyrenes, which may be incorporated into polyester molecules during polycondensation or are physically mixed with polymer in the fiber formation process. In this article we present an alternative method to reduce the flammability of PET fibers and fabrics which is analogous to dyeing them with a dispersed dyes in a high temperature bath. We have tested this method many times using various modifiers so far. This time, we applied a commercial organophilized montmorillonite Cloisite (R) 15A (C15A). In the presented work, using Limited Oxygen Index (LOI) flammability tests and the thermogravimetric analysis (TGA) method, the effectiveness of the modification used was demonstrated and its optimal variant was determined. Based on Fourier Transform-Infrared Spectroscopy (FT-IR) studies, the existence of interactions between PET macromolecules and the C15A modifier in the entire temperature range of the oxidative degradation was confirmed. Using the Wide-Angle X-ray Scattering (WAXS) and Small-Angle X-ray Scattering (SAXS) methods, the basic parameters of the nano-structure of the studied fibers were determined, and their nanocomposite nature was confirmed. The most important goal, which was successfully achieved, was to explain the mechanism of flame inhibition by the applied modifier C15A.