Carbon Nanoparticles/Polyvinyl Alcohol Composites With Enhanced Optical, Thermal, Mechanical, And Flame-Retardant Properties

In this work, polyvinyl alcohol (PVA) is chemically bonded to carbon nanoparticles (CNPs) by a very simple and versatile solution casting method. Five different kinds of CNPs/PVA composite films were prepared; 0.5, 1.0, 1.5, 2.0, and 3.0 wt% CNPs dispersed in PVA. The as-prepared samples were characterized using various characterization techniques. The resulting nanocomposites proved to possess homogeneity and better mechanical, thermal, optical, and flame-retardant properties than pure PVA. Most of the CNPs with average particle size <= 100 nm were homogeneously dispersed in the PVA matrix showing fluorescence in the violet color zone. The crystallinity of the nanocomposites show a decline in the diffraction intensity as compared to pure PVA which results from the dwelling of CNPs inside the gaps of stacked-layer chains of PVA. The mechanical properties of nanocomposites indicated enhancement in toughness, elastic modulus and tensile strength with an increase in CNPs contents. The assessment for flame-retardant properties was carried out through cone calorimetry. The results show a decrease in both total heat release rate (THRR) and peak heat release rate (pHRR) of the resulting nanocomposites as compared to pure PVA. The superior properties of the CNPs/PVA composites stemmed from the good interfacial bonding between the CNPs and PVA matrix.