Wettability and In-Vitro Study of Titanium Surface Profiling Prepared by Electrolytic Plasma Processing.

Electrolytic plasma processing (EPP) was used to create hydrophilic surface profiles on titanium. The wettability, surface morphology characteristics and chemical composition of the treated samples were studied as a function of EPP processing parameters. The EPP profiled surfaces comprised of a characteristic "hills and valleys" morphology because of continuous surface melting and freezing cycles. A bimodal surface profile was produced with 2-3 μm height hills and valleys with nano-roughness (≤200 nm). The produced profile resulted in a significant contact angle decrease (from 38.7° to 5.4°). Ratios of actual surface area to projection area (r) and fraction of solid surface remaining dry (φ) were obtained from profilometry. The surface characteristics and large r values produced by EPP were able to induce hemi-wicking. Hence, EPP produced superhydrophilic surfaces on Ti. The bioactivity of EPP treated Ti was evaluated using cell free and MC3T3 cells in-vitro studies. The treated Ti surface significantly increased the bioactivity and formed stoichiometric hydroxyapatite after immersion in a bone cell culture medium for 21 days. Cells' attachment and proliferation studies indicated that EPP treated surface significantly enhances the cells' adhesion and growth after 24 and 48 h compared to the untreated surface. The results show that Ti surface profiling by EPP constitutes a promising method to potentially improve bone implant bonding.