Bacterial Exposure To Nickel: Influence On Adhesion And Biofilm Formation On Orthodontic Archwires And Sensitivity To Antimicrobial Agents
MATERIALS(2021)
摘要
The presence of nickel could modify bacterial behavior and susceptibility to antimicrobial agents. Adhesion and biofilm formation on orthodontic archwires can be a source of bacterial colonization and possible health hazards. Staphylococcus aureus was subjected to exposure and adaptation to various sub-inhibitory concentrations of nickel. Five strains of bacteria adapted to nickel in concentrations of 62.5-1000 mu g/mL were tested for adhesion and biofilm formation on nickel-titanium archwires. Archwires were previously incubated in artificial saliva. Bacteria were incubated with orthodontic wire with stirring for 4 h (adhesion) and 24 h (biofilm formation). The number of adherent bacteria was determined after sonication and cultivation on the Muller-Hinton agar. Disk diffusion method was performed on all bacteria to assess the differences in antimicrobial susceptibility. Bacteria adapted to lower concentrations of nickel adhered better to nickel-titanium than strains adapted to higher concentrations of nickel (p < 0.05). Biofilm formation was highest in strains adapted to 250 and 500 mu g/mL of nickel (p < 0.05). The highest biofilm biomass was measured for strains adapted to 250 mu g/mL, followed by those adapted to 1000 mu g/mL. Bacteria adapted to lower concentrations of nickel demonstrated lower inhibition zone diameters in the disk diffusion method (p < 0.05), indicating increased antimicrobial resistance. In conclusion, bacteria adapted to 250 mu g/mL of nickel ions adhered better, demonstrated higher biofilm formation and often had higher antimicrobial resistance than other adapted and non-adapted strains.
更多查看译文
关键词
bacteria, nickel, biofilm, adhesion, orthodontic archwire, antimicrobial resistance
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要