Enhancing The Oxidation Resistance Of Al2o3-Sic-C Castables Via Introducing Micronized Andalusite

Additions of andalusite aggregates (19 wt%) were shown in previous literature to enhance the antioxidation of Al2O3-SiC-C (ASC) castables. This work aims to investigate whether micronized andalusite has a greater influence on antioxidation improvement than andalusite aggregates. Various low contents (5 wt% and below) of micronized andalusite (<= 5 mu m) were introduced as a substitute for brown fused alumina in the matrix of ASC castables. The antioxidation of castable specimens was estimated by the oxidized area ratio on the fracture surface after a thermal shock test. The microstructure and phases of micronized andalusite and the castable specimens were characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD), respectively. The results suggest that the antioxidation effects of ASC castables with a low addition of micronized andalusite are effectively enhanced. The heat-induced transformation of andalusite produces SiO2-rich glass, favoring the sintering of the castable matrix and impeding oxygen diffusion into the castable's interior. Therefore, the castable antioxidation is enhanced without deteriorating the hot modulus of rupture.