Pore-size control of chitin nanofibrous composite membrane using metal-organic frameworks.

Herein, environmentally benign chitin nanofiber (ChNF) membranes were fabricated by regulating suspension behavior. The introduction of zeolitic imidazole frameworks (ZIF-8) into the composite membranes led to the domain formation of ChNF derived by coordinative interaction, resulting in pore size-tunable membranes. Based on the rheological, morphological, and structural characterizations, the driving force of pore-size control was studied in the aqueous suspension of ChNF and ZIF-8 according to the relative concentration. At critical concentration, the 30-ChNF membrane presents superior water permeance (40 LMH h-1) while maintaining a high rejection rate (>80% for all organic dyes). Moreover, the molecular size cut-off of the composite membranes for dyes can be controlled in the range of less than 1 nm to 2 nm. The experimental results provide a simple strategy for the preparation of pore tunable ChNF membranes using MOF with high mechanical strength, good durability, high flux, dye rejection, and antifouling ability.