A General Strategy Towards Superhydrophobic Self-Cleaning And Anti-Corrosion Metallic Surfaces: An Example With Aluminum Alloy

Corrosion and contamination of metallic structures can cause loss of their functionality as well as aesthetic values. In this study, we describe a general strategy to prepare superhydrophobic self-cleaning and anti-corrosion surfaces for metallic structures. As a specific example, a superhydrophobic coating (SHC) on aluminum alloy was prepared by a simple etching combined with the decoration of a low-surface-energy material. The optimal SHC has a water contact angle (CA) at similar to 157.4 degrees and a sliding angle (SA) of similar to 8.3 degrees due to the synergy of binary hierarchical structures and chemical modification. The SHC showed low adhesion to dry contaminants and a series of liquids, displaying a good self-cleaning effect. The SHC maintained superhydrophobicity after exposure to air and humid condition at 60 degrees C for 7 days. In addition, the electrochemical measurements reveal that the anti-corrosion performance was enhanced by reducing the corrosion current density (J(corr)) by 1 order of magnitude and increasing the corrosion potential (E-corr) by 0.527 V as compared to the bare Al alloy substrate after immersion for 168 h.