Layered Double Hydroxides Intercalated With Methyl Orange As A Controlled-Release Corrosion Inhibitor For Iron In Chloride Media

In this study, the corrosion inhibition properties of nanocontainer-type layered double hydroxide (LDH) are evaluated on iron that is immersed in a 3.5% NaCl aqueous solution. LDH ZnAl-NO3 was synthesized via coprecipitation. The material presents satisfactory crystallinity with a Zn/Al ratio of 2:1. Methyl orange (MO) has been added into the synthesis process by exchange with nitrate ions and/or by adsorption of MO onto LDH surfaces (LDH-MO). Iron was immersed in solutions with various concentrations of LDH and LDH-MO ranged 1-6 gl(-1), and the corrosion inhibition properties were investigated using linear sweep votammetry, electrochemical impedance spectroscopy (EIS), and SEM. Based on pitting potential studies, LDH has demonstrated inhibition of the pitting corrosion process, and the optimal concentration was identified as 2 gl(-1). The presence of MO in LDH provides excellent anticorrosive properties with a mixed inhibition mechanism. The corrosion potential of LDH-MO presents more noble values and exchange current densities that are one order of magnitude less than those of the bare iron after 72 h of immersion in a 3.5% NaCl aqueous solution. EIS results corroborated that the corrosion resistance increased when 2 gl(-1) of LDH-MO was in solution. SEM images support the anticorrosive behaviour of the LDH-MO.