Lanthanum strontium cobaltite as interconnect in oxide thermoelectric generators

Issues related to use of metallic interconnects in oxide thermoelectric generators (TEGs) need to be addressed to secure performance and durability. Metal interconnects suffer from high cost of noble metals or chemical instability and contact resistance of non-noble metals, arising from oxidation, evaporation, and delamination in the oxidising conditions of ambient air at high operating temperatures. This work introduces the use of a stable and highly conducting ceramic oxide, in our case p-type lanthanum strontium cobaltite (La0.6Sr0.4CoO3, LSC) as interconnect. We verified the thermochemical stability of LSC in contact with p-type Ni0.98Li0.02O (Li–NiO) and n-type Zn0.98Al0.02O (Al–ZnO) and examined the electrical characteristics. An area specific contact resistance (ASRc) of ∼1800 Ω cm2 for a direct p-n junction was reduced to ∼400 mΩ cm2 for a p-LSC-n junction at a temperature of 300 °C, validating the concept. The use of a screen-printed LSC/Al–ZnO composite as a thin interconnect layer was found to decrease the contact resistance of the junction further to ∼260 mΩ cm2 at 300 °C, attributed to increased effective area of the LSC/Al–ZnO p-n junction.