Simple synthetic route to Ca18.75Li10.5[Al39N55]:Ce3+ yellow-green phosphors for white LEDs
OPTICAL MATERIALS EXPRESS(2022)
摘要
Nitride phosphors usually have great influence on the performance of white LEDs. However, most nitrides require synthesis under high temperature and high pressure, especially Ca18.75Li10.5[Al39N55] (CLAN), which demands preparation even under a pressure of 51.7 MPa. Herein, we applied a simple synthetic route to obtain CLAN at a low pressure of 0.85 MPa and temperature of 1250 degrees C. In addition, the luminescence properties of Ce3+ doped CLAN were studied and the CLAN:Ce3+ shows three excitation bands peaked at 267, 387, and 478 nm. Two emission peaks are located at 513 nm and 567 nm, corresponding to the d-f electronic transition of Ce3+, respectively. The emission intensity at 150 degrees C retains about 83.3% of the initial value at room temperature, indicating a good thermal stability. A prototype white LED encapsulated with a 450 nm chip and the CLAN:Ce3+ phosphor exhibits bright white emission, indicating potential applications. (C) 2022 Optica Publishing Group under the terms of the Optica Open Access Publishing Agreement
更多查看译文
关键词
leds,simple synthetic route,ca<sub>1875</sub>li<sub>105</sub>al<sub>39</sub>n<sub>55</sub>ce<sup>3+</sup>,yellow-green
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要