Cooperative effect between copper species and oxygen vacancy in Ce0.7-xZrxCu0.3O2 catalysts for carbon monoxide oxidation

The effects of Zr doping on the existence of Cu and the catalytic performance of Ce0.7-xZrxCu0.3O2 for CO oxidation were investigated. The characterization results showed that all samples have a cubic structure, and a small amount of Zr doping facilitates Cu2+ ions entering the CeO2 lattice, but excessive Zr doping leads to the formation of surface CuO crystals again. Thus, the number of oxygen vacancies caused by the Cu2+ entering the lattice (e.g., Cu2+-rectangle-Ce4+; rectangle: oxygen vacancy), and the amount of reducible copper species caused by CuO crystals, varies with the Zr doping. Catalytic CO oxidation tests indicated that the oxygen vacancy and the reducible copper species were the adsorption and activation sites of O-2 and CO, respectively, and the cooperative effects between them accounted for the high CO oxidation activity. Thus, the samples x = 0.1 and 0.3, which possessed the most oxygen vacancy or reducible copper species, showed the best activity for CO oxidation, with full CO conversion obtained at 110 degrees C. The catalyst is also stable and has good resistance to water during the reaction.