PROPERTIES OF TUBES FROM Zr-1% Nb ALLOY AFTER THERMOCHEMICAL TREATMENT AND HYDROGENATION

The influence of treatment in controlled gas environments with subsequent hydrogenation on the physical and mechanical characteristics of the Zr-1% Nb zirconium alloy has been investigated. The surface hardness and the size of the diffusion-hardened layer of the ring-samples cut from fuel tubes from the Zr-1% Nb alloy after treatment in oxygen- and nitrogen-containing gaseous media with subsequent saturation with hydrogen have been established. The influence of the parameters of the gaseous medium and the modes of thermochemical treatment (TCT) of specimens-rings on the destructive stresses under static load at temperatures of 20 and 380 degrees C is shown. It was revealed that treatment in the investigated gas environment increases the resistance to hydrogen saturation and has a positive effect on the long-term strength of ring specimens from the zirconium alloy Zr-1% Nb.