Studying the combined influence of microplastics' intrinsic and extrinsic characteristics on their weathering behavior and heavy metal transport in storm runoff

The weathering and contaminant transport behavior of both primary (PMPs) and secondary microplastics (SMPs) are interrelated to their original physiochemical features and variations within the environment. This study examines the influence of PMPs' intrinsic characteristics (polymer structure and crystallinity) and SMPs' extrinsic features (surface oxidation and external sediments attachment) on the photodegradation kinetics, and subsequently Pb(II) and Zn(II) uptake from stormwater. For this purpose, high density polyethylene (HDPE) and low density polyethylene (LDPE) with different degrees of crystallinities were produced as PMPs, and their photodegradation behaviors were compared with original polymers. Furthermore, the SMPs generated by abrasion and surface oxidation of PMPs and the virgin PMPs underwent accelerated photodegradation, and the changes of their crystallinity, surface chemistry, and morphology were examined. Scanning electron microscopy (SEM) imaging and X-ray photoelectron (XPS) studies revealed the formation of cracks and different oxidized functionalities on MPs surface due to UV photodegradation. The vinyl and carbonyl indices calculated using Attenuated Total Reflectance Fourier Transform Infrared (ATR-FTIR) spectroscopy demonstrated an elevated photodegradation rate for SMPs compared to the PMPs. Moreover, the Differential Scanning Colorimetry (DSC) demonstrated an increasing percentage of crystallinity in all MPs due to the photodegradation. The percent crystallinity of HDPE pellets increased after photodegradation from 49.8 to 62.6 and it increased from 17.2 to 38.9 for LDPE pellets respectively. The greater level of increase in crystallinity for LDPE in comparison to HDPE upon photodegradation was referred to as LDPE's greater amorphous content and branched structure. A greater level of metal uptake was obtained for photodegraded LDPE pellets as 2526 mu g/m(2) for Pb(II) and 2028 mu g/m(2) for Zn(II) respectively.