Dynamic strain aging and microstructural damage mechanism of austenitic stainless steel under thermomechanical fatigue in the temperature range of 250–400 °C

•The increase in strain amplitude enhances the influence of phase angle on fatigue life.•The dynamic strain aging is only observed at strain amplitude of 0.6%.•Dislocation cell structures formed at high strain amplitude accelerate the softening rate and reduce fatigue life.