Influence of Artificial Aging on Mechanical Properties of Six Resin Composite Blocks for CAD/CAM Application

(1) The interactions in the oral cavity between resin composite blocks for CAD/CAM application and saliva, biofilm, and chemicals and their influence on mechanical properties are still mostly unknown. The purpose of this study is to examine the impact of artificial aging on the flexural strength, flexural modulus, hardness, Weibull modulus, and probability of failure of six resin composite CAD/CAM materials. (2) The aging was conducted by storing the specimens in water at 37 degrees C for 3 months, then a 3-point bending test was applied and measured. The microhardness was measured with a Vickers microhardness tester. Weibull analysis (according to ISO) was also performed. The shape and scale parameters were calculated. (3) After aging, the flexural strength values ranged from 95.51 (SD 9.07) MPa for the aged Shofu Block HC (HC) to 160.28 (SD 10.37) MPa for non-aged Gandio blocks (GR), and the flexural modulus values ranged from 7.75 (SD 0.19) GPa for HC to 16.77 (SD 0.60) GPa for GR. The microhardness (HV01) ranged from 72.71 (SD 1.43) for the Katana Avencia Block (AV) to 140.50 (SD 5.51) for GR. After aging, the Weibull characteristic strength ranged from 99.47 MPa for HC to 169.25 MPA for Brilliant Crios (CR). (4) Water storage led to a decrease in flexural strength and characteristic strength and slightly affected the flexural modulus. Gandio Blocks, Tetric CAD, and Brilliant Crios presented higher flexural strength than others.