Processing, Microstructure, and Mechanical Properties of Laser Additive Manufactured Ti2AlNb-Based Alloy with Carbon, Boron, and Yttrium Microalloying

In this work, Ti-22Al-23Nb-0.8Mo-0.3Si-0.4C-0.1B-0.2Y (at. %) alloy powder was used to fabricate the Ti2AlNb-based alloy samples using Laser powder bed fusion (L-PBF) Additive Manufacturing with a high-temperature substrate preheating. L-PBF process parameters, including laser power, scan speed, hatching distance, and preheating temperature, allowing for obtaining fully dense (99.9% relative density) crack-free samples, were determined. The effects of substrate preheating temperature during the L-PBF process on microstructure, phase composition, and properties of the obtained Ti2AlNb-based alloy were investigated using X-ray diffraction, scanning electron microscopy, electron backscatter diffraction analysis, and microhardness testing. The results obtained for the material with C, B, and Y microalloying were compared to the Ti2AlNb-based alloy fabricated by L-PBF from the powder not alloyed with C, B, and Y. The results revealed that the microalloying reduced the number of solidification cracks; however, no significant microstructural changes were observed, and high-temperature substrate preheating was still necessary to suppress cold cracking of the alloy. The microstructure of the alloy varied from fully-beta/B2, B2 + O, to fully-O depending on the preheating temperature. Effects of hot isostatic pressing and heat treatment conditions on microstructure and mechanical properties were investigated.