Synthesis and Properties of Optically Transparent Fluoro-Containing Polyimide Films with Reduced Linear Coefficients of Thermal Expansion from Organo-Soluble Resins Derived from Aromatic Diamine with Benzanilide Units

Wholly aromatic polyimide (PI) films with good solution processability, light colors, good optical transparency, high storage modulus, and improved heat resistance were prepared and characterized. For this purpose, a multi-component copolymerization methodology was performed from a fluoro-containing dianhydride, 4,4'-(hexafluoroisopropylidene)diphthalic anhydride (6FDA), a rigid dianhydride, 3,3',4,4'-biphenyltetracarboxylic dianhydride (BPDA), and a fluoro-containing diamine, 2,2'-bis(trifluoromethyl)-4,4'-bis [4-(4-amino-3-methyl)benzamide]biphenyl (MABTFMB). One homopolymer, FPI-1 (6FDA-MABTFMB), and five copolymers, FPI-2 similar to FPI-6, containing the BPDA units from 10 mol% to 50 mol% in the dianhydride moieties, were prepared, respectively. The derived PI resins showed good solubility in the polar aprotic solvents, such as N-methyl-2-pyrrolidone (NMP) and N,N-dimethylacetamide (DMAc). The flexible PI films obtained by the solution casting procedure showed good optical properties with the transmittances higher than 74.0% at the wavelength of 450 nm. The PI films exhibited excellent thermal properties, including 5% weight loss temperatures (T-5%) over 510 degrees C, together with glass transition temperatures (T-g) over 350.0 degrees C according to the peak temperatures of the loss modulus in dynamical mechanical analysis (DMA) measurements. The FPI-6 film also showed the lowest linear coefficient of thermal expansion (CTE) value of 23.4 x 10(-6)/K from 50 to 250 degrees C according to the thermomechanical analysis (TMA) measurements, which was obviously lower than that of FPI-1 (CTE = 30.6 x 10(-6)/K).