Behaviour of polymer-coated composite nanoparticles at bubble-stabilizing interfaces during bubble coarsening and accelerated coalescence: A Cryo-SEM study

The 0.1 M bubble-stabilizing interface buckles in uniaxial compression due to coarsening, with the CPs being observed to desorb from the interface. While the CPs were visualized to rearrange into crumpled particle multi-layers surrounding the shrinking 0.55 M bubbles, due to the adhesion between interpenetrating polymer chains and the unique lubrication effect of the PVP layers. The 0.1 M to 0.55 M transition foaming behaviour was also studied. Cracks and voids were observed at interfaces surrounding the transition bubbles driven by in-situ particle aggregation, resulting in accelerated bubble coalescence during the transition process.