Preparation of Ag-CeO2-LSCF composite catalyst and its catalytic performance for soot
INORGANIC CHEMISTRY COMMUNICATIONS(2022)
摘要
In this paper, La0.6Sr0.4Co0.2Fe0.8O3 (LSCF) perovskite catalyst was prepared and compounded with Ag and CeO2 by impregnation method to synthesize Ag-CeO2-LSCF(A-C-L) composite catalyst. The change of catalytic soot performance of LSCF catalyst before and after composite was studied. The results show that the microstructure of A-C-L composite catalyst is good, and the characteristic temperature values of soot are 344.0 degrees C, 394.8 degrees C and 445.1 degrees C, respectively, which are 56.9 degrees C, 56.5 degrees C and 51.5 degrees C lower than those of LSCF. When the content of Ag is 8 wt%, the catalytic performance of A-C-L composite catalyst is the best.
更多查看译文
关键词
Soot, Composite catalyst, Oxidation