Eco-friendly preparation and structural characterization of calcium silicates derived from eggshell and silica gel

In this work, the preparation of calcium-silicate-based composites consisting of natural waste from calcium source as eggshell and silica gel from a desiccator as a silicon source both presenting alternative materials for cheap preparation of eco-friendly calcium-silicate bioceramics has been investigated. The effect of the CaO/SiO2 ratio on microstructural properties has also been studied. The pseudowollastonite formation has been observed in the case of 40 wt.% CaO and 60 wt.% SiO2 with lowest porosity and highest density 2.6 g/cm(3). In the case of 50 wt.% CaO and 50 wt.% SiO2, the phase transformation from pseudowollastonite to wollastonite was observed. Increasing the calcium content caused higher apparent porosity with 19%. It was shown that the development of novel ceramics from reused waste, eggshell, or silica can be an optimal solution for the low-cost preparation of calcium silicates with potential applications in medicine or cement, food industry.