Eu3+ -activated red phosphor Ca3 YAl3 B4 O15 with low thermal quenching behaviour.

This paper reports a sequence of a Ca3 YAl3 B4 O15 :xEu3+ red phosphor prepared using a high-temperature solid-state reaction. At the excitation of 396 nm, the samples emitted intense red emission centred at ~623 nm, which could be attributed to the 5 D0 →7 F2 transition of the Eu3+ ion. The results showed that the optimum Eu3+ doping concentration of Ca3 YAl3 B4 O15 :Eu3+ phosphor was x = 80 mol%, and the concentration quenching mechanism of Ca3 YAl3 B4 O15 :Eu3+ red phosphor belonged to the exchange coupling between Eu3+ ions. The Commission Internationale de l'éclairage (CIE) coordinates and colour purity of Ca3 Y0.2 Al3 B4 O15 :0.8Eu3+ were calculated as (0.6375, 0.3476) and 95.5%, respectively. Moreover, the red emission of the obtained phosphor Ca3 YAl3 B4 O15 :0.8Eu3+ exhibited a low thermal quenching behaviour with an intensity retention rate of 92.85% at 150°C. The above results manifest that the Eu3+ -activated Ca3 YAl3 B4 O15 phosphor is predicted to be a promising red luminescent component for white light-emitting diodes.