A new basic burning raw material for simultaneous stabilization/solidification of PO43−-P and F− in phosphogypsum

Phosphogypsum (PG) contains a lot of soluble phosphate (PO43--P) and fluorine ion (F-), which seriously has hindered the sustainable development of the phosphorous chemical industry. In this study, a new burning raw material (BRM) as an intermediate product in the cement production process was used for PO43--P and F- stabilize in PG. The stabilizing mechanism of PO43--P and F- were investigated by Fourier Transform infrared spectroscopy (FT-IR), X-ray diffractometer (XRD), Scanning Electron Microscopy (SEM), X-ray fluorescence (XRF) and X-ray spectroscopy system (XPS). The effect of PG and BRM weight ratio, solid-to-liquid ratio, reaction time, and reaction temperature on the concentrations of PO43--P and F- were studied. The results showed that the concentration of F- in the PG leaching solution was 8.65 mg/L and the stabilizing efficiency of PO43--P was 99.78%, as well as the pH of the PG leaching solution was 8.12 when the weight ratio of PG and BRM was 100:2, and the solid to liquid ratio was 4:1, reacting for 24 h at the temperature of 30 ℃. PO43--P and F- were mostly solidified as Ca5(PO4)3F, CaPO3(OH), Ca5(PO4)3(OH), Ca2P2O7·2H2O, CaSO4PO3(OH)·4H2O, CaF2, and CaFPO3·2H2O. Leaching test results indicated that the concentrations of PO43--P, F- and heavy metals were less than the integrated wastewater discharge standard (GB8978–1996). This study provides a new harmless treatment method for PG.