Wide-Temperature Tunable Phonon Thermal Switch Based on Ferroelectric Domain Walls of Tetragonal KTN Single Crystal

Ferroelectric domain walls (DWs) of perovskite oxide materials, which can be written and erased by an external electric field, offer the possibility to dynamically manipulate phonon scattering and thermal flux behavior. Different from previous ferroelectric materials, such as BaTiO3, PbTiO3, etc., with an immutable and low Curie temperature. The Curie temperature of perovskite oxide KTa1-xNbxO3 (KTN) crystal can be tuned by altering the Ta/Nb ratio. In this work, the ferroelectric KTa0.6Nb0.4O3 (KTN) single crystal is obtained by the Czochralski method. To understand the role of ferroelectric domains in thermal transport behavior, we perform a nonequilibrium molecular dynamics (NEMD) calculation on monodomain and 90 degrees DWs of KTN at room temperature. The calculated thermal conductivity of monodomain KTN is 9.84 W/(m center dot k), consistent with experimental results of 8.96 W/(m center dot k), and distinctly decreased with the number of DWs indicating the outstanding performance of the thermal switch. We further evaluate the thermal boundary resistance (TBR) of KTN DWs. An interfacial thermal resistance value of 2.29 x 10(-9) K center dot m(2)/W and a large thermal switch ratio of 4.76 was obtained for a single DW of KTN. Our study shows that the ferroelectric KTN can provide great potential for the application of thermal switch at room temperature and over a broad temperature range.