Effect of Lubricating Oil and Wiper on Super-High Strength 7055 Aluminum Alloy Ingots

The casting table with lubricating oil and wiper is applied simultaneously to produce super-high-strength 7055 aluminum alloy (Al7055) ingots, and 30 T Al7055 ingots with a diameter of 582 mm were cast successfully. In this study, the microstructure and macrosegregation of the ingots were investigated using an optical microscope (OM). The research results show that the hydrogen content in the liquid metal can be decreased from 0.198 mL/100 g Al to 0.103 mL/100 g Al when three rotors are used in the degassing tank. Compared with the conventional hot-top casting table, the surface quality can be improved by using the casting table with oil lubrication. The temperature gradient between the ingot center and edge can be decreased by using the wiper during the casting process from 320 degrees C to 150 degrees C, the cracking tendency caused by the ingot temperature gradient can be decreased, the segregation layer thickness is decreased by about 87%, and the ingot can be homogenized at a high temperature by using the heat of the feed itself.