Multimodal Luminescent Low-Dimension Cs2ZrCl6:xSb(3+) Crystals for White Light-Emitting Diodes and Information Encryption

Low-dimension perovskite materials have attracted wide attention due to their excellent optical properties and stability. Herein, Sb3+-doped Cs2ZrCl6 crystals are synthesized by a coprecipitation method in which Sb3+ ions partially replace Zr4+ ions. The Cs2ZrCl6:xSb(3+) powder shows blue and orange-red emissions under a 254 and 365 nm light, respectively, due to the [ZrCl6](2-) octahedron and [SbCl6](3-) octahedron. The photoluminescence quantum yield (PLQY) of Cs2ZrCl6:xSb(3+) (x = 0.1) crystals is up to 52.5%. According to experimental and computational results, the emission mechanism of the Cs2ZrCl6:xSb(3+) crystals is proposed. On the one hand, a wide blue emission with a large Stokes shift is caused by the self-trapping excitons of [ZrCl6]2- octahedra under a 260 nm excitation. On the other hand, the luminescence mechanism of [SbCl6]3- octahedron is divided into two parts: 1P1-* 1S0 (490 nm) and 3P1-* 1S0 (625 nm). The broad-band emission, high PLQY, and excellent stability endow the Cs2ZrCl6:xSb(3+) powders with the potential for the fabrication of white light-emitting diodes (WLEDs). A WLED device is fabricated using a commercial 310 nm NUV chip, which shows a high color rendering index of 89.7 and a correlated color temperature of 5333 K. In addition, the synthesized Cs2ZrCl6:xSb(3+) crystals can be also successfully used for information encryption. Our work will provide a deep understanding of the photophysical properties of Sb3+-doped perovskites and facilitate the development of Cs2ZrCl6:xSb(3+) crystals in encrypting multilevel optical codes and WLEDs.