Glass-Ceramic Protective Coatings Based on Metallurgical Slag

Pyroxene glass-ceramic enamels based on combinations of blast furnace slag and some additives were produced and investigated. The batch compositions and technological regimes of enameling were developed to produce high temperature protective coatings for carbon steel (ASTM 1010/1008). The composition of raw materials was selected to match the values of the thermal expansion coefficients of the glass-ceramic coating (similar to 11 center dot 10(-6) K-1) and metal substrate (similar to 12 center dot 10(-6) K-1) taking into account the temperatures of fluidization (T-f similar to 800 degrees) and crystallization (T-c = 850-1020 degrees C) of the corresponding glasses. The covered and thermally treated samples of carbon steel were produced using single-layer enameling technology and investigated to specify structure, phase composition and properties of the coating and coating-steel interface. The obtained coatings were characterized with excellent adhesion to the steel (impact energy similar to 3 J) and protective properties. The closed porous structure of the coatings promoted low thermal conductivity (similar to 1 W/(m center dot K)) and high (up to 1000 degrees C) thermal resistance, whereas the pyroxene-like crystalline phases supported high wear and chemical resistance as well as micro-hardness (similar to 480 MPa) and thermal shock resistance (>30 cycles of 23-700 degrees C). The obtained cheap coatings and effective protective coatings could be used at the temperatures up to 1100 degrees C in the corrosive atmosphere and under the action of abrasive particles.