Enhancement effect of RuO2 doping on the reduction process of NOx by NH3 via V2O5-WO3/TiO2 particle catalyst under low-temperature: Structure-activity relationship and reaction mechanism

As a mainstream moderate-high temperature (250-420 degrees C) particulate denitrification catalyst, V2O5-WO3/TiO2 (VWT) is not applicable to low-temperature (60-150 degrees C) iron ore sintering flue gas after semi dry/wet desul-furization. In order to improve the NH3-deNOx performance of the VWT particle catalyst at low temperatures, a series of powder VWT denitrification catalysts doped with different content of RuO2 (R-VWT) prepared by the wet co-impregnation method were researched, and found that the particulate catalyst service temperature (about 100 % NO conversion) is lowered from 225 degrees C (VWT) to below 175 degrees C by doping 0.5 % RuO2. In addition, a series of characterizations indicate that the doped RuO2 enhances the redox performance of R-VWT and promotes the generation of more surface active intermediate monodentate nitrate, and accelerates the low-temperature surface SCR transient reaction rate.